PRODUCTS DESCRIPTION:
Annealed Wire is made of carbon steel wire, used for weaving, baling in general. Applied for home use and the construction.
Annealed wire is obtained by means of thermal annealing, endowing it with the properties it needs for its main use - setting. This wire is deployed both in civil construction and in agriculture. Hence, in civil construction annealed wire, also known as "burnt wire" is used for iron setting. In agriculture annealed wire is used for bailing hay.
Annealed wire for civil construction:
The annealing of bare wire (wire which has simply been drawn) can be carried out in batches (bell-type furnace) or in line (in-line furnace).
Annealing is intended to return to the wire its ductility which it had lost during drawing.
Annealed wire is stored in coils or spools of a varying weights and dimensions depending on the purposes for which it is intended and the needs of clients. The product does not usually have any type of protective lining, paper or plastic. We offer two kinds of annealed wire, bright annealed and black annealed wire. Black annealed wire gets its name from its plain black color.
Soft annealed wire offers excellent flexibility and softness through the process of oxygen free annealing.
Packing: Spools, coils.
TECHNOLOGY DETAIL
| Carbon spring steel wires | |||
| Suitable for using the springs in machinery | GB4357-89 | ||
| Diameter mm | Tensile Strength ,MPa | ||
| B | C | D | |
| 0.40 | 1910-2300 | 2250-2650 | 2600-2990 |
| 0.45 | 1860-2260 | 2200-2600 | 2550-2940 |
| 0.50 | 1860-2260 | 2200-2600 | 2550-2940 |
| 0.55 | 1810-2210 | 2150-2550 | 2500-2890 |
| 0.60 | 1760-2160 | 2110-2500 | 2450-2840 |
| 0.63 | 1760-2160 | 2110-2500 | 2450-2840 |
| 0.70 | 1710-2110 | 2060-2450 | 2450-2840 |
| 0.80 | 1710-2060 | 2010-2400 | 2400-2840 |
| 0.90 | 1710-2060 | 2010-2350 | 2350-2750 |
| 1.00 | 1660-2010 | 1960-2300 | 2300-2690 |
| 1.20 | 1620-1960 | 1910-2250 | 2250-2550 |
| 1.40 | 1620-1910 | 1860-2210 | 2150-2450 |
| 1.60 | 1570-1860 | 1810-2160 | 2100-2400 |
| 1.80 | 1520-1810 | 1760-2110 | 2010-2300 |
| 2.00 | 1470-1760 | 1710-2010 | 1910-2200 |
| 2.20 | 1420-1710 | 1660-1960 | 1810-2110 |
| 2.50 | 1420-1710 | 1660-1960 | 1760-2060 |
| 2.80 | 1370-1670 | 1620-1910 | 1710-2010 |
| 3.00 | 1370-1670 | 1570-1860 | 1710-1960 |
| 3.20 | 1320-1620 | 1570-1810 | 1660-1910 |
| 3.50 | 1320-1620 | 1570-1810 | 1660-1910 |
| 4.00 | 1320-1620 | 1570-1760 | 1620-1860 |
| 4.50 | 1320-1570 | 1520-1760 | 1620-1860 |
Tensile strength table of steel wire(Mpa)
| Group | Tensile strength |
| A1 | 1180-1380 |
| A2 | 1380-1580 |
| A3 | 1580-1780 |
| A4 | 1780-1980 |
| A5 | 1980-2180 |
| A6 | 2180-2380 |
Diameter tolerance of steel wire
| Diameter of steel wire(mm) | Grade of allowable tolerance | ||
| h10 | h11 | h12 | |
| Allowable tolerance | |||
| >0.30-0.60 | ±0.01 | ±0.02 | ±0.03 |
| >0.60-1.00 | ±0.01 | ±0.02 | ±0.03 |
| >1.00-3.00 | ±0.02 | ±0.03 | ±0.05 |
| >3.00-5.00 | ±0.02 | ±0.03 | ±0.05 |